Blast furnace








Former blast furnace in Port of Sagunto, Valencia, Spain.


A blast furnace is a type of metallurgical furnace used for smelting to produce industrial metals, generally pig iron, but also others such as lead or copper. Blast refers to the combustion air being "forced" or supplied above atmospheric pressure.[1]


In a blast furnace, fuel (coke), ores, and flux (limestone) are continuously supplied through the top of the furnace, while a hot blast of air (sometimes with oxygen enrichment) is blown into the lower section of the furnace through a series of pipes called tuyeres, so that the chemical reactions take place throughout the furnace as the material falls downward. The end products are usually molten metal and slag phases tapped from the bottom, and waste gases (flue gas) exiting from the top of the furnace. The downward flow of the ore and flux in contact with an upflow of hot, carbon monoxide-rich combustion gases is a countercurrent exchange and chemical reaction process.[2]


In contrast, air furnaces (such as reverberatory furnaces) are naturally aspirated, usually by the convection of hot gases in a chimney flue. According to this broad definition, bloomeries for iron, blowing houses for tin, and smelt mills for lead would be classified as blast furnaces. However, the term has usually been limited to those used for smelting iron ore to produce pig iron, an intermediate material used in the production of commercial iron and steel, and the shaft furnaces used in combination with sinter plants in base metals smelting.[3][4]




Contents






  • 1 History


    • 1.1 China


    • 1.2 Medieval Europe


      • 1.2.1 Catalan forges


      • 1.2.2 Oldest European blast furnaces


      • 1.2.3 Cistercian contributions






  • 2 Origin and spread of early modern blast furnaces


    • 2.1 Coke blast furnaces


    • 2.2 Steam-powered blast


    • 2.3 Hot blast


    • 2.4 Modern furnaces


      • 2.4.1 Iron blast furnaces


      • 2.4.2 Lead blast furnaces


      • 2.4.3 Zinc blast furnaces (Imperial Smelting Furnaces)






  • 3 Modern process


  • 4 Process engineering and chemistry


  • 5 Manufacture of stone wool


  • 6 Decommissioned blast furnaces as museum sites


  • 7 Gas cleaning systems


  • 8 Gallery


  • 9 See also


  • 10 References


    • 10.1 Bibliography




  • 11 External links





History




An illustration of furnace bellows operated by waterwheels, from the Nong Shu, by Wang Zhen, 1313, during the Yuan Dynasty of China




Chinese fining and blast furnace, Tiangong Kaiwu, 1637.


See also: History of ferrous metallurgy

Cast iron has been found in China dating to the 5th century BC, but the earliest extant blast furnaces in China date to the 1st century AD and in the West from the High Middle Ages.[5] They spread from the region around Namur in Wallonia (Belgium) in the late 15th century, being introduced to England in 1491. The fuel used in these was invariably charcoal. The successful substitution of coke for charcoal is widely attributed to English inventor Abraham Darby in 1709. The efficiency of the process was further enhanced by the practice of preheating the combustion air (hot blast), patented by Scottish inventor James Beaumont Neilson in 1828.[6]



China


See also: History of metallurgy in China

Archaeological evidence shows that bloomeries appeared in China around 800 BC. Originally it was thought that the Chinese started casting iron right from the beginning, but this theory has since been debunked by the discovery of 'more than ten' iron digging implements found in the tomb of Duke Jing of Qin (d. 537 BC), whose tomb is located in Fengxiang County, Shaanxi (a museum exists on the site today).[7] There is however no evidence of the bloomery in China after the appearance of the blast furnace and cast iron. In China blast furnaces produced cast iron, which was then either converted into finished implements in a cupola furnace, or turned into wrought iron in a fining hearth.[8]


Although cast iron farm tools and weapons were widespread in China by the 5th century BC, employing workforces of over 200 men in iron smelters from the 3rd century onward, the earliest extant blast furnaces were built date to the Han Dynasty in the 1st century AD.[9] These early furnaces had clay walls and used phosphorus-containing minerals as a flux.[10] Chinese blast furnaces ranged from around two to ten meters in height, depending on the region. The largest ones were found in modern Sichuan and Guangdong, while the 'dwarf" blast furnaces were found in Dabieshan. In construction, they are both around the same level of technological sophistication [11]


The effectiveness of the Chinese blast furnace was enhanced during this period by the engineer Du Shi (c. AD 31), who applied the power of waterwheels to piston-bellows in forging cast iron.[12] Donald Wagner suggests that early blast furnace and cast iron production evolved from furnaces used to melt bronze. Certainly, though, iron was essential to military success by the time the State of Qin had unified China (221 BC). Usage of the blast and cupola furnace remained widespread during the Song and Tang Dynasties.[13] By the 11th century, the Song Dynasty Chinese iron industry made a switch of resources from charcoal to coke in casting iron and steel, sparing thousands of acres of woodland from felling. This may have happened as early as the 4th century AD.[14][15]


The primary advantage of the early blast furnace was in large scale production and making iron implements more readily available to peasants.[16] Cast iron is more brittle than wrought iron or steel, which required additional fining and then cementation or co-fusion to produce, but for menial activities such as farming it sufficed. By using the blast furnace, it was possible to produce larger quantities of tools such as ploughshares more efficiently than the bloomery. In areas where quality was important, such as warfare, wrought iron and steel were preferred. Nearly all Han period weapons are made of wrought iron or steel, with the exception of axe-heads, of which many are made of cast iron.[17]


Blast furnaces were also later used to produce gunpowder weapons such as cast iron bomb shells and cast iron cannons during the Song dynasty.[18]



Medieval Europe



Catalan forges


The simplest forge, known as the Corsican, was used prior to the advent of Christianity. Examples of improved bloomeries are the Stückofen [fr][19] (sometimes called wolf-furnace[20]) or the Catalan forge, which remained until the beginning of the 19th century. The Catalan forge was invented in Catalonia, Spain, during the 8th century. Instead of using natural draught, air was pumped in by a trompe, resulting in better quality iron and an increased capacity. This pumping of airstream in with bellows is known as cold blast, and it increases the fuel efficiency of the bloomery and improves yield. The Catalan forges can also be built bigger than natural draught bloomeries.



Oldest European blast furnaces




The first blast furnace of Germany as depicted in a miniature in the Deutsches Museum


The oldest known blast furnaces in the West were built in Dürstel in Switzerland, the Märkische Sauerland in Germany, and at Lapphyttan in Sweden, where the complex was active between 1205 and 1300.[21] At Noraskog in the Swedish parish of Järnboås, there have also been found traces of blast furnaces dated even earlier, possibly to around 1100.[22] These early blast furnaces, like the Chinese examples, were very inefficient compared to those used today. The iron from the Lapphyttan complex was used to produce balls of wrought iron known as osmonds, and these were traded internationally – a possible reference occurs in a treaty with Novgorod from 1203 and several certain references in accounts of English customs from the 1250s and 1320s. Other furnaces of the 13th to 15th centuries have been identified in Westphalia.[23]


The technology required for blast furnaces may have either been transferred from China, or may have been an indigenous innovation. Al-Qazvini in the 13th century and other travellers subsequently noted an iron industry in the Alburz Mountains to the south of the Caspian Sea. This is close to the silk route, so that the use of technology derived from China is conceivable. Much later descriptions record blast furnaces about three metres high.[24] As the Varangian Rus' people from Scandinavia traded with the Caspian (using their Volga trade route, it is possible that the technology reached Sweden by this means.[25] High quality ores, water power for bellows for blast and wood for charcoal are readily obtainable in Sweden. However, since blast furnace has also been invented independently in Africa by the Haya people, it is more likely the process has been invented in Scandinavia independently. The step from bloomery to true blast furnace is not big. Simply just building a bigger furnace and using bigger bellows to increase the volume of the blast and hence the amount of oxygen leads inevitably into higher temperatures, bloom melting into liquid iron and, cast iron flowing from the smelters. Already the Vikings are known to have used double bellows, which greatly increases the volumetric flow of the blast.[26]


This Caspian region may also separately be the technological source for at furnace at Ferriere, described by Filarete.[27] Water-powered bellows at Semogo [it] in northern Italy in 1226 in a two-stage process. In this, the molten iron was tapped twice a day into water thereby granulating it.[28]



Cistercian contributions


One means by which certain technological advances were transmitted within Europe was a result of the General Chapter of the Cistercian monks. This may have included the blast furnace, as the Cistercians are known to have been skilled metallurgists.[29] According to Jean Gimpel, their high level of industrial technology facilitated the diffusion of new techniques: "Every monastery had a model factory, often as large as the church and only several feet away, and waterpower drove the machinery of the various industries located on its floor." Iron ore deposits were often donated to the monks along with forges to extract the iron, and within time surpluses were being offered for sale. The Cistercians became the leading iron producers in Champagne, France, from the mid-13th century to the 17th century,[30] also using the phosphate-rich slag from their furnaces as an agricultural fertilizer.[31]


Archaeologists are still discovering the extent of Cistercian technology.[32] At Laskill, an outstation of Rievaulx Abbey and the only medieval blast furnace so far identified in Britain, the slag produced was low in iron content.[33] Slag from other furnaces of the time contained a substantial concentration of iron, whereas Laskill is believed to have produced cast iron quite efficiently.[33][34][35] Its date is not yet clear, but it probably did not survive until Henry VIII's Dissolution of the Monasteries in the late 1530s, as an agreement (immediately after that) concerning the "smythes" with the Earl of Rutland in 1541 refers to blooms.[36] Nevertheless, the means by which the blast furnace spread in medieval Europe has not finally been determined.



Origin and spread of early modern blast furnaces




Period drawing of an 18th-century blast furnace


Due to the casting of cannon, the blast furnace came into widespread use in France in the mid 15th century.[37][38]


The direct ancestor of these used in France and England was in the Namur region in what is now Wallonia (Belgium). From there, they spread first to the Pays de Bray on the eastern boundary of Normandy and from there to the Weald of Sussex, where the first furnace (called Queenstock) in Buxted was built in about 1491, followed by one at Newbridge in Ashdown Forest in 1496. They remained few in number until about 1530 but many were built in the following decades in the Weald, where the iron industry perhaps reached its peak about 1590. Most of the pig iron from these furnaces was taken to finery forges for the production of bar iron.[39]


The first British furnaces outside the Weald appeared during the 1550s, and many were built in the remainder of that century and the following ones. The output of the industry probably peaked about 1620, and was followed by a slow decline until the early 18th century. This was apparently because it was more economic to import iron from Sweden and elsewhere than to make it in some more remote British locations. Charcoal that was economically available to the industry was probably being consumed as fast as the wood to make it grew.[40] The Backbarrow blast furnace built in Cumbria in 1711 has been described as the first efficient example.[who?]


The first blast furnace in Russia opened in 1637 near Tula and was called the Gorodishche Works. The blast furnace spread from here to the central Russia and then finally to the Urals.[41]



Coke blast furnaces




The original blast furnaces at Blists Hill, Coalbrookdale




Charging the experimental blast furnace, Fixed Nitrogen Research Laboratory, 1930


In 1709, at Coalbrookdale in Shropshire, England, Abraham Darby began to fuel a blast furnace with coke instead of charcoal. Coke's initial advantage was its lower cost, mainly because making coke required much less labor than cutting trees and making charcoal, but using coke also overcame localized shortages of wood, especially in Britain and on the Continent. Metallurgical grade coke will bear heavier weight than charcoal, allowing larger furnaces.[42][43] A disadvantage is that coke contains more impurities than charcoal, with sulfur being especially detrimental to the iron's quality. Coke's impurities were more of a problem before hot blast reduced the amount of coke required and before furnace temperatures were hot enough to make slag from limestone free flowing. (Limestone ties up sulfur. Manganese may also be added to tie up sulfur).[44]:123-125[45][46][37]:122-23


Coke iron was initially only used for foundry work, making pots and other cast iron goods. Foundry work was a minor branch of the industry, but Darby's son built a new furnace at nearby Horsehay, and began to supply the owners of finery forges with coke pig iron for the production of bar iron. Coke pig iron was by this time cheaper to produce than charcoal pig iron. The use of a coal-derived fuel in the iron industry was a key factor in the British Industrial Revolution.[47][48][49] Darby's original blast furnace has been archaeologically excavated and can be seen in situ at Coalbrookdale, part of the Ironbridge Gorge Museums. Cast iron from the furnace was used to make girders for the world's first iron bridge in 1779. The Iron Bridge crosses the River Severn at Coalbrookdale and remains in use for pedestrians.



Steam-powered blast


The steam engine was applied to power blast air, overcoming a shortage of water power in areas where coal and iron ore were located. The cast iron blowing cylinder was developed in 1768 to replace the leather bellows, which wore out quickly. The steam engine and cast iron blowing cylinder led to a large increase in British iron production in the late 18th century.[37]



Hot blast


Hot Blast was the single most important advance in fuel efficiency of the blast furnace and was one of the most important technologies developed during the Industrial Revolution.[50][51]Hot blast was patented by James Beaumont Neilson at Wilsontown Ironworks in Scotland in 1828. Within a few years of the introduction, hot blast was developed to the point where fuel consumption was cut by one-third using coke or two-thirds using coal, while furnace capacity was also significantly increased. Within a few decades, the practice was to have a "stove" as large as the furnace next to it into which the waste gas (containing CO) from the furnace was directed and burnt. The resultant heat was used to preheat the air blown into the furnace.[52]


Hot blast enabled the use of raw anthracite coal, which was difficult to light, to the blast furnace. Anthracite was first tried successfully by George Crane at Ynyscedwyn Ironworks in south Wales in 1837.[53] It was taken up in America by the Lehigh Crane Iron Company at Catasauqua, Pennsylvania, in 1839. Anthracite use declined when very high capacity blast furnaces requiring coke were built in the 1870s.



Modern furnaces



Iron blast furnaces


The blast furnace remains an important part of modern iron production. Modern furnaces are highly efficient, including Cowper stoves to pre-heat the blast air and employ recovery systems to extract the heat from the hot gases exiting the furnace. Competition in industry drives higher production rates. The largest blast furnaces have a volume around 5,580 m3 (197,000 cu ft)[54] and can produce around 80,000 tonnes (79,000 long tons; 88,000 short tons) of iron per week.[needs update]


This is a great increase from the typical 18th-century furnaces, which averaged about 360 tonnes (350 long tons; 400 short tons) per year. Variations of the blast furnace, such as the Swedish electric blast furnace, have been developed in countries which have no native coal resources.



Lead blast furnaces


Blast furnaces are currently rarely used in copper smelting, but modern lead smelting blast furnaces are much shorter than iron blast furnaces and are rectangular in shape.[55] The overall shaft height is around 5 to 6 m.[56] Modern lead blast furnaces are constructed using water-cooled steel or copper jackets for the walls, and have no refractory linings in the side walls.[55] The base of the furnace is a hearth of refractory material (bricks or castable refractory).[55] Lead blast furnaces are often open-topped rather than having the charging bell used in iron blast furnaces.[57]


The blast furnace used at the Nyrstar Port Pirie lead smelter differs from most other lead blast furnaces in that it has a double row of tuyeres rather than the single row normally used.[56] The lower shaft of the furnace has a chair shape with the lower part of the shaft being narrower than the upper.[56] The lower row of tuyeres being located in the narrow part of the shaft.[56] This allows the upper part of the shaft to be wider than the standard.[56]



Zinc blast furnaces (Imperial Smelting Furnaces)


The blast furnaces used in the Imperial Smelting Process ("ISP") were developed from the standard lead blast furnace, but are fully sealed.[58] This is because the zinc produced by these furnaces is recovered as metal from the vapor phase, and the presence of oxygen in the off-gas would result in the formation of zinc oxide.[58]


Blast furnaces used in the ISP have a more intense operation than standard lead blast furnaces, with higher air blast rates per m2 of hearth area and a higher coke consumption.[58]


Zinc production with the ISP is more expensive than with electrolytic zinc plants, so several smelters operating this technology have closed in recent years.[59] However, ISP furnaces have the advantage of being able to treat zinc concentrates containing higher levels of lead than can electrolytic zinc plants.[58]



Modern process





Blast furnace placed in an installation

  1. Iron ore + limestone sinter

  2. Coke

  3. Elevator

  4. Feedstock inlet

  5. Layer of coke

  6. Layer of sinter pellets of ore and limestone

  7. Hot blast (around 1200 °C)

  8. Removal of slag

  9. Tapping of molten pig iron

  10. Slag pot

  11. Torpedo car for pig iron

  12. Dust cyclone for separation of solid particles

  13. Cowper stoves for hot blast

  14. Smoke outlet (can be redirected to carbon capture & storage (CCS) tank)

  15. Feed air for Cowper stoves (air pre-heaters)

  16. Powdered coal

  17. Coke oven

  18. Coke

  19. Blast furnace gas downcomer







Blast furnace diagram


  1. Hot blast from Cowper stoves

  2. Melting zone (bosh)

  3. Reduction zone of ferrous oxide (barrel)

  4. Reduction zone of ferric oxide (stack)

  5. Pre-heating zone (throat)

  6. Feed of ore, limestone, and coke

  7. Exhaust gases

  8. Column of ore, coke and limestone

  9. Removal of slag

  10. Tapping of molten pig iron

  11. Collection of waste gases




Modern furnaces are equipped with an array of supporting facilities to increase efficiency, such as ore storage yards where barges are unloaded. The raw materials are transferred to the stockhouse complex by ore bridges, or rail hoppers and ore transfer cars. Rail-mounted scale cars or computer controlled weight hoppers weigh out the various raw materials to yield the desired hot metal and slag chemistry. The raw materials are brought to the top of the blast furnace via a skip car powered by winches or conveyor belts.[60]


There are different ways in which the raw materials are charged into the blast furnace. Some blast furnaces use a "double bell" system where two "bells" are used to control the entry of raw material into the blast furnace. The purpose of the two bells is to minimize the loss of hot gases in the blast furnace. First, the raw materials are emptied into the upper or small bell which then opens to empty the charge into the large bell. The small bell then closes, to seal the blast furnace, while the large bell rotates to provide specific distribution of materials before dispensing the charge into the blast furnace.[61][62] A more recent design is to use a "bell-less" system. These systems use multiple hoppers to contain each raw material, which is then discharged into the blast furnace through valves.[61] These valves are more accurate at controlling how much of each constituent is added, as compared to the skip or conveyor system, thereby increasing the efficiency of the furnace. Some of these bell-less systems also implement a discharge chute in the throat of the furnace (as with the Paul Wurth top) in order to precisely control where the charge is placed.[63]


The iron making blast furnace itself is built in the form of a tall structure, lined with refractory brick, and profiled to allow for expansion of the charged materials as they heat during their descent, and subsequent reduction in size as melting starts to occur. Coke, limestone flux, and iron ore (iron oxide) are charged into the top of the furnace in a precise filling order which helps control gas flow and the chemical reactions inside the furnace. Four "uptakes" allow the hot, dirty gas high in carbon monoxide content to exit the furnace throat, while "bleeder valves" protect the top of the furnace from sudden gas pressure surges. The coarse particles in the exhaust gas settle in the "dust catcher" and are dumped into a railroad car or truck for disposal, while the gas itself flows through a venturi scrubber and/or electrostatic precipitators and a gas cooler to reduce the temperature of the cleaned gas.[60]


The "casthouse" at the bottom half of the furnace contains the bustle pipe, water cooled copper tuyeres and the equipment for casting the liquid iron and slag. Once a "taphole" is drilled through the refractory clay plug, liquid iron and slag flow down a trough through a "skimmer" opening, separating the iron and slag. Modern, larger blast furnaces may have as many as four tapholes and two casthouses.[60] Once the pig iron and slag has been tapped, the taphole is again plugged with refractory clay.




Tuyeres of Blast Furnace at Gerdau, Brazil


The tuyeres are used to implement a hot blast, which is used to increase the efficiency of the blast furnace. The hot blast is directed into the furnace through water-cooled copper nozzles called tuyeres near the base. The hot blast temperature can be from 900 °C to 1300 °C (1600 °F to 2300 °F) depending on the stove design and condition. The temperatures they deal with may be 2000 °C to 2300 °C (3600 °F to 4200 °F). Oil, tar, natural gas, powdered coal and oxygen can also be injected into the furnace at tuyere level to combine with the coke to release additional energy and increase the percentage of reducing gases present which is necessary to increase productivity.[60]



Process engineering and chemistry




Blast furnaces of Třinec Iron and Steel Works, Czech Republic


Blast furnaces operate on the principle of chemical reduction whereby carbon monoxide, having a stronger affinity for the oxygen in iron ore than iron does, reduces the iron to its elemental form. Blast furnaces differ from bloomeries and reverberatory furnaces in that in a blast furnace, flue gas is in direct contact with the ore and iron, allowing carbon monoxide to diffuse into the ore and reduce the iron oxide to elemental iron mixed with carbon. The blast furnaces operates as a countercurrent exchange process whereas a bloomery does not. Another difference is that bloomeries operate as a batch process while blast furnaces operate continuously for long periods because they are difficult to start up and shut down. (See: Continuous production) Also, the carbon in pig iron lowers the melting point below that of steel or pure iron; in contrast, iron does not melt in a bloomery.


Carbon monoxide also reduces silica which has to be removed from the pig iron. The silica is reacted with calcium oxide (burned limestone) and forms a slag which floats to the surface of the molten pig iron. The direct contact of flue gas with the iron causes contamination with sulfur if it is present in the fuel. Historically, to prevent contamination from sulfur, the best quality iron was produced with charcoal.


The downward moving column of ore, flux, coke or charcoal and reaction products must be porous enough for the flue gas to pass through. This requires the coke or charcoal to be in large enough particles to be permeable, meaning there cannot be an excess of fine particles. Therefore, the coke must be strong enough so it will not be crushed by the weight of the material above it. Besides physical strength of the coke, it must also be low in sulfur, phosphorus, and ash. This necessitates the use of metallurgical coal, which is a premium grade due to its relative scarcity.


The main chemical reaction producing the molten iron is:


Fe2O3 + 3CO → 2Fe + 3CO2[64]

This reaction might be divided into multiple steps, with the first being that preheated blast air blown into the furnace reacts with the carbon in the form of coke to produce carbon monoxide and heat:


2 C(s) + O2(g) → 2 CO(g)[65]

The hot carbon monoxide is the reducing agent for the iron ore and reacts with the iron oxide to produce molten iron and carbon dioxide. Depending on the temperature in the different parts of the furnace (warmest at the bottom) the iron is reduced in several steps. At the top, where the temperature usually is in the range between 200 °C and 700 °C, the iron oxide is partially reduced to iron(II,III) oxide, Fe3O4.


3 Fe2O3(s) + CO(g) → 2 Fe3O4(s) + CO2(g)[65]

At temperatures around 850 °C, further down in the furnace, the iron(II,III) is reduced further to iron(II) oxide:


Fe3O4(s) + CO(g) → 3 FeO(s) + CO2(g)[65]

Hot carbon dioxide, unreacted carbon monoxide, and nitrogen from the air pass up through the furnace as fresh feed material travels down into the reaction zone. As the material travels downward, the counter-current gases both preheat the feed charge and decompose the limestone to calcium oxide and carbon dioxide:


CaCO3(s) → CaO(s) + CO2(g)[65]

The calcium oxide formed by decomposition reacts with various acidic impurities in the iron (notably silica), to form a fayalitic slag which is essentially calcium silicate, CaSiO3:[64]


SiO2 + CaO → CaSiO3[66][better source needed]

As the iron(II) oxide moves down to the area with higher temperatures, ranging up to 1200 °C degrees, it is reduced further to iron metal:


FeO(s) + CO(g) → Fe(s) + CO2(g)[65]

The carbon dioxide formed in this process is re-reduced to carbon monoxide by the coke:


C(s) + CO2(g) → 2 CO(g)[65]

The temperature-dependent equilibrium controlling the gas atmosphere in the furnace is called the Boudouard reaction:


2CO ⇌ CO2 + C

The "pig iron" produced by the blast furnace has a relatively high carbon content of around 4–5%, making it very brittle, and of limited immediate commercial use. Some pig iron is used to make cast iron. The majority of pig iron produced by blast furnaces undergoes further processing to reduce the carbon content and produce various grades of steel used for construction materials, automobiles, ships and machinery.


Although the efficiency of blast furnaces is constantly evolving, the chemical process inside the blast furnace remains the same. According to the American Iron and Steel Institute: "Blast furnaces will survive into the next millennium because the larger, efficient furnaces can produce hot metal at costs competitive with other iron making technologies."[60] One of the biggest drawbacks of the blast furnaces is the inevitable carbon dioxide production as iron is reduced from iron oxides by carbon and as of 2016, there is no economical substitute – steelmaking is one of the largest industrial contributors of the CO2 emissions in the world (see greenhouse gases).


The challenge set by the greenhouse gas emissions of the blast furnace is being addressed in an ongoing European Program called ULCOS (Ultra Low CO2 Steelmaking).[67] Several new process routes have been proposed and investigated in depth to cut specific emissions (CO2 per ton of steel) by at least 50%. Some rely on the capture and further storage (CCS) of CO2, while others choose decarbonizing iron and steel production, by turning to hydrogen, electricity and biomass.[68] In the nearer term, a technology that incorporates CCS into the blast furnace process itself and is called the Top-Gas Recycling Blast Furnace is under development, with a scale-up to a commercial size blast furnace under way. The technology should be fully demonstrated by the end of the 2010s, in line with the timeline set, for example, by the EU to cut emissions significantly. Broad deployment could take place from 2020 on.[citation needed]



Manufacture of stone wool


Stone wool or rock wool is a spun mineral fibre used as an insulation product and in hydroponics. It is manufactured in a blast furnace fed with diabase rock which contains very low levels of metal oxides. The resultant slag is drawn off and spun to form the rock wool product.[69] Very small amounts of metals are also produced which are an unwanted by-product and run to waste.



Decommissioned blast furnaces as museum sites


Main article: List of preserved historic blast furnaces

For a long time, it was normal procedure for a decommissioned blast furnace to be demolished and either be replaced with a newer, improved one, or to have the entire site demolished to make room for follow-up use of the area. In recent decades, several countries have realized the value of blast furnaces as a part of their industrial history. Rather than being demolished, abandoned steel mills were turned into museums or integrated into multi-purpose parks. The largest number of preserved historic blast furnaces exists in Germany; other such sites exist in Spain, France, the Czech Republic, Japan, Luxembourg, Poland, Romania, Mexico, Russia and the United States.



Gas cleaning systems


The blast furnace gas can be used to generate heat. So by reducing the constituents in blast furnace gas we can increase the calorific value and can be used to generate heat and rise the temperature in any furnace.


The gas cleaning system contains two stages, the coarse cleaning system and the fine cleaning system.


In the coarse cleaning system a dust catcher is used. A dust catcher is a cylindrical steel structure with conical top and bottom sections. It is also lined with refractory bricks.



Dust catcher drawing.png


The principle of the dust catcher is that the dust-laden gas is given a sudden reverse in speed and direction. Because of their mass, the coarse dust particles cannot change their velocity easily, and hence settle to the bottom.



Gallery






  • Blast furnace in Sestao, Spain. The furnace itself is inside the central girderwork.







  • Part of the gas cleaning system of a blast furnace in Monclova, Mexico. This one is about to be de-commissioned and replaced.






See also



  • Basic oxygen furnace

  • Blast furnace zinc smelting process

  • Crucible steel

  • Extraction of iron


  • Water gas, produced by a "steam blast"

  • FINEX

  • Flodin process


  • Ironworks and steelworks in England, which covers ironworks of all kinds.

  • Laskill



References





  1. ^ See: Draft (boiler)


  2. ^ Development of heat transfer circuits in the blast furnace, IOP Conference Series: Materials Science and Engineering


  3. ^ P J Wand, "Copper smelting at Electrolytic Refining and Smelting Company of Australia Ltd., Port Kembla, N.S.W.", in: Mining and Metallurgical Practices in Australasia: The Sir Maurice Mawby Memorial Volume, Ed J T Woodcock (The Australasian Institute of Mining and Metallurgy: Melbourne, 1980) 335–340.


  4. ^ R J Sinclair, The Extractive Metallurgy of Lead (The Australasian Institute of Mining and Metallurgy: Melbourne, 2009), 9–12.


  5. ^ Peter J. Golas (25 February 1999). Science and Civilisation in China: Volume 5, Chemistry and Chemical Technology, Part 13, Mining. Cambridge University Press. p. 152. ISBN 978-0-521-58000-7. ...earliest blast furnace discovered in China from about the first century AD.mw-parser-output cite.citation{font-style:inherit}.mw-parser-output q{quotes:"""""""'""'"}.mw-parser-output code.cs1-code{color:inherit;background:inherit;border:inherit;padding:inherit}.mw-parser-output .cs1-lock-free a{background:url("//upload.wikimedia.org/wikipedia/commons/thumb/6/65/Lock-green.svg/9px-Lock-green.svg.png")no-repeat;background-position:right .1em center}.mw-parser-output .cs1-lock-limited a,.mw-parser-output .cs1-lock-registration a{background:url("//upload.wikimedia.org/wikipedia/commons/thumb/d/d6/Lock-gray-alt-2.svg/9px-Lock-gray-alt-2.svg.png")no-repeat;background-position:right .1em center}.mw-parser-output .cs1-lock-subscription a{background:url("//upload.wikimedia.org/wikipedia/commons/thumb/a/aa/Lock-red-alt-2.svg/9px-Lock-red-alt-2.svg.png")no-repeat;background-position:right .1em center}.mw-parser-output .cs1-subscription,.mw-parser-output .cs1-registration{color:#555}.mw-parser-output .cs1-subscription span,.mw-parser-output .cs1-registration span{border-bottom:1px dotted;cursor:help}.mw-parser-output .cs1-hidden-error{display:none;font-size:100%}.mw-parser-output .cs1-visible-error{font-size:100%}.mw-parser-output .cs1-subscription,.mw-parser-output .cs1-registration,.mw-parser-output .cs1-format{font-size:95%}.mw-parser-output .cs1-kern-left,.mw-parser-output .cs1-kern-wl-left{padding-left:0.2em}.mw-parser-output .cs1-kern-right,.mw-parser-output .cs1-kern-wl-right{padding-right:0.2em}


  6. ^ Simcoe, Charles R. "The Age Of Steel: Part II." Advanced Materials & Processes 172.4 (2014): 32-33. Academic Search Premier.


  7. ^ "The Earliest Use of Iron in China" by Donald B. Wagner in Metals in Antiquity, by Suzanne M. M. Young, A. Mark Pollard, Paul Budd and Robert A. Ixer (BAR International Series, 792), Oxford: Archaeopress, 1999, pp. 1–9.


  8. ^ Wagner 2008, p. 230.


  9. ^ Ebrey, p. 30.


  10. ^ Early iron in China, Korea, and Japan Archived 5 February 2007 at the Wayback Machine., Donald B. Wagner, March 1993


  11. ^ Wagner 2008, p. 6.


  12. ^ Needham, Joseph (1986), Science and Civilisation in China, Volume 4: Physics and Physical Technology, Part 2, Mechanical Engineering, Taipei: Cambridge University Press, p. 370, ISBN 0-521-05803-1


  13. ^ The Coming of the Ages of Steel. Brill Archive. p. 54. GGKEY:DN6SZTCNQ3G.


  14. ^ Donald B. Wagner, 'Chinese blast furnaces from the 10th to the 14th century' Historical Metallurgy 37(1) (2003), 25–37; originally published in West Asian Science, Technology, and Medicine 18 (2001), 41–74.


  15. ^ Ebrey, p. 158.


  16. ^ Wagner 2008, p. 169.


  17. ^ Wagner 2008, p. 1.


  18. ^ Liang 2006.


  19. ^ Julius H. Strassburger (1969). Blast Furnace-theory and Practice. Gordon and Breach Science Publishers. p. 4. ISBN 978-0-677-10420-1. Retrieved 12 July 2012.


  20. ^ Douglas Alan Fisher, Excerpt from The Epic of Steel Archived 25 February 2007 at the Wayback Machine., Davis Town Museum & Harper & Row, NY 1963.


  21. ^ Jockenhövel, Albrecht et al. (1997) "Archaeological Investigations on the Beginning of Blast Furnace-Technology in Central Europe" Archived 11 March 2012 at WebCite Abteilung für Ur- und Frühgeschichtliche Archäologie, Westfälische Wilhelms-Universität Münster; abstract published as: Jockenhövel, A. (1997) "Archaeological Investigations on the Beginning of Blast Furnace-Technology in Central Europe" pp. 56–58 In Crew, Peter and Crew, Susan (editors) (1997) Early Ironworking in Europe: Archaeology and Experiment: Abstracts of the International Conference at Plas Tan y Bwlch 19–25 September 1997 (Plas Tan y Bwlch Occasional Papers No 3) Snowdonia National Park Study Centre, Gwynedd, Wales,
    OCLC 470699473; archived here [1] by WebCite on 11 March 2012


  22. ^ A. Wetterholm, 'Blast furnace studies in Nora bergslag' (Örebro universitet 1999, Järn och Samhälle)
    ISBN 91-7668-204-8


  23. ^ N. Bjökenstam, 'The Blast Furnace in Europe during the Middle Ages: part of a new system for producing wrought iron' in G. Magnusson, The Importance of Ironmaking: Technological Innovation and Social Change I (Jernkontoret, Stockholm 1995), 143–53 and other papers in the same volume.


  24. ^ Wagner 2008, 349–51.


  25. ^ Wagner 2008, 354.


  26. ^ "Adventures in Early Iron Production - An overview of experimental iron smelts, 2001 - 2005, by Darrell Markewitz. Bloomery iron furnaces of the Viking Age, experimental archaeology wrought iron production". www.warehamforge.ca. Archived from the original on 22 September 2015.


  27. ^ Wagner 2008, 355.


  28. ^ B. G. Awty, 'The blast funace in the Renaissance period: haut fournau or fonderie ', Transactions of Newcomen Society 61 (1989–90). 67.


  29. ^ Woods, p. 34.


  30. ^ Gimpel, p. 67.


  31. ^ Woods, p. 35.


  32. ^ Woods, p. 36.


  33. ^ ab Woods, p. 37.


  34. ^ R. W. Vernon, G. McDonnell and A. Schmidt (1998). "An integrated geophysical and analytical appraisal of early iron-working: three case studies". Historical Metallurgy. 32 (2): 72–5, &nbsp, 79.


  35. ^ David Derbyshire, 'Henry "Stamped Out Industrial Revolution"' Archived 13 June 2014 at the Wayback Machine., The Daily Telegraph (21 June 2002); cited by Woods.


  36. ^ Schubert, H. R. (1957), History of the British iron and steel industry from c. 450 BC to AD 1775, Routledge & Kegan Paul, pp. 395–397


  37. ^ abc Tylecote, R. F. (1992). A History of Metallurgy, Second Edition. London: Maney Publishing, for the Institute of Materials. ISBN 978-0901462886.


  38. ^ Merson, John (1990). The Genius That Was China: East and West in the Making of the Modern World. Woodstock, New York: The Overlook Press. p. 69. ISBN 0-87951-397-7A companion to the PBS Series “The Genius That Was China”


  39. ^ B. Awty & C. Whittick (with P. Combes), 'The Lordship of Canterbury, iron-founding at Buxted, and the continental antecedents of cannon-founding in the Weald' Sussex Archaeological Collections 140 (2004 for 2002), pp. 71–81.


  40. ^ P. W. King, 'The production and consumption of iron in early modern England and Wales' Economic History Review LVIII(1), 1–33; G. Hammersley, 'The charcoal iron industry and its fuel 1540–1750' Economic History Review Ser. II, XXVI (1973), pp. 593–613.


  41. ^ Yakovlev, V. B. (1957), "Development of Wrought Iron Production", Metallurgist, New York: Springer, 1 (8): 545, doi:10.1007/BF00732452


  42. ^
    Landes, David. S. (1969). The Unbound Prometheus: Technological Change and Industrial Development in Western Europe from 1750 to the Present. Cambridge, New York: Press Syndicate of the University of Cambridge. pp. 90–93. ISBN 0-521-09418-6.


  43. ^
    Rosen, William (2012). The Most Powerful Idea in the World: A Story of Steam, Industry and Invention. University Of Chicago Press. p. 149. ISBN 978-0226726342.


  44. ^ Tylecote, R. F. (1992). A History of Metallurgy, Second Edition. London: Maney Publishing, for the Institute of Materials. ISBN 978-0901462886.


  45. ^ McNeil, Ian (1990). An Encyclopedia of the History of Technology. London: Routledge. ISBN 0415147921.


  46. ^ "Coke for Blast Furnace Ironmaking". steel.org. Archived from the original on 8 February 2017.


  47. ^ Raistrick, Arthur (1953), Dynasty of Iron Founders: The Darbys and Coalbrookedale, York: Longmans, Green


  48. ^ Hyde


  49. ^ Trinder, Barrie Stuart; Trinder, Barrie (2000), The Industrial Revolution in Shropshire, Chichester: Phillimore, ISBN 1-86077-133-5


  50. ^
    Landes, David. S. (1969). The Unbound Prometheus: Technological Change and Industrial Development in Western Europe from 1750 to the Present. Cambridge, New York: Press Syndicate of the University of Cambridge. p. 92. ISBN 0-521-09418-6.


  51. ^ Ayres, Robert (1989). "Technological Transformations and Long Waves" (PDF): 21. Archived (PDF) from the original on 7 July 2012<Fig. 7 shows C/Fe ratio time series>


  52. ^ Birch, pp. 181–9.


  53. ^ Hyde, p. 159.


  54. ^ Only together we shall susseed!, archived from the original on 1 February 2009, retrieved 2008-05-20


  55. ^ abc R J Sinclair, The Extractive Metallurgy of Lead (The Australasian Institute of Mining and Metallurgy: Melbourne, 2009), 75.


  56. ^ abcde R J Sinclair, The Extractive Metallurgy of Lead (The Australasian Institute of Mining and Metallurgy: Melbourne, 2009), 77.


  57. ^ R J Sinclair, The Extractive Metallurgy of Lead (The Australasian Institute of Mining and Metallurgy: Melbourne, 2009), 76.


  58. ^ abcd R J Sinclair, The Extractive Metallurgy of Lead (The Australasian Institute of Mining and Metallurgy: Melbourne, 2009), 89.


  59. ^ R J Sinclair, The Extractive Metallurgy of Lead (The Australasian Institute of Mining and Metallurgy: Melbourne, 2009), 90.


  60. ^ abcde American Iron and Steel Institute (2005). How a Blast Furnace Works. steel.org.


  61. ^ ab McNeil, Ian (1990), An encyclopaedia of the history of technology, Taylor & Francis, p. 163, ISBN 0-415-01306-2


  62. ^ Strassburger, Julius H. (1969), Blast furnace: Theory and Practice, Taylor & Francis, p. 564, ISBN 0-677-10420-0


  63. ^ Whitfield, Peter, Design and Operation of a Gimbal Top Charging System (PDF), archived from the original (PDF) on 5 March 2009, retrieved 2008-06-22


  64. ^ ab "Blast Furnace". Science Aid. Archived from the original on 17 December 2007. Retrieved 30 December 2007.


  65. ^ abcdef Rayner-Canham & Overton (2006), Descriptive Inorganic Chemistry, Fourth Edition, New York: W. H. Freeman and Company, pp. 534–535, ISBN 978-0-7167-7695-6


  66. ^ Dr. K. E Lee, Form Two Science (Biology Chemistry Physics)


  67. ^ http://www.ulcos.org Archived 21 November 2008 at the Wayback Machine.


  68. ^ ICIT-Revue de Métallurgie, September and October issues, 2009


  69. ^ What is stone wool? rockwool.co.uk




Bibliography


.mw-parser-output .refbegin{font-size:90%;margin-bottom:0.5em}.mw-parser-output .refbegin-hanging-indents>ul{list-style-type:none;margin-left:0}.mw-parser-output .refbegin-hanging-indents>ul>li,.mw-parser-output .refbegin-hanging-indents>dl>dd{margin-left:0;padding-left:3.2em;text-indent:-3.2em;list-style:none}.mw-parser-output .refbegin-100{font-size:100%}



  • Birch, Alan (2005), The Economic History of the British Iron and Steel Industry, 1784–1879, Routledge, ISBN 0-415-38248-3


  • Ebrey, Patricia Buckley; Walthall, Anne; Palais, James B. (2005), East Asia: A Cultural, Social, and Political History, Boston: Houghton Mifflin, ISBN 0-618-13384-4


  • Gimpel, Jean (1976), The Medieval Machine: The Industrial Revolution of the Middle Ages, New York: Holt, Rinehart and Winston, ISBN 0-03-014636-4


  • Hyde, Charles K. (1977), Technological Change and the British iron industry, 1700–1870, Princeton: Princeton University Press, ISBN 0-691-05246-8


  • Liang, Jieming (2006), Chinese Siege Warfare: Mechanical Artillery & Siege Weapons of Antiquity, Singapore, Republic of Singapore: Leong Kit Meng, ISBN 981-05-5380-3


  • Wagner, Donald B. (2008), Science and Civilization in China Volume 5-11: Ferrous Metallurgy, Cambridge University Press


  • Woods, Thomas (2005), How the Catholic Church Built Western Civilization, Washington, D.C.: Regnery Publ., ISBN 0-89526-038-7




External links







  • American Iron and Steel Institute

  • Blast Furnace animation

  • Extensive picture gallery about all methods of making and shaping of iron and steel in North America and Europe. In German and English.

  • Schematic diagram of blast furnace and Cowper stove












-

Popular posts from this blog

Eastern Orthodox Church

Image
Not to be confused with Oriental Orthodoxy, Eastern Christianity, or Eastern Catholic Churches. "Eastern Orthodoxy", "Orthodox Church", "Orthodox Catholic Church", and "Orthodox Christian Church" redirect here. For other uses, see Orthodox (disambiguation). This article may be too long to read and navigate comfortably . The readable prose size is 132 kilobytes. Please consider splitting content into sub-articles, condensing it, or adding or removing subheadings. ( January 2018 ) Part of a series on the Eastern Orthodox Church Mosaic of Christ Pantocrator, Hagia Sophia Overview Structure Theology (History of theology) Liturgy Church history Holy Mysteries View of salvation View of Mary View of icons Background Crucifixion / Resurrection / Ascension of Jesus Christianity Christian Church Apostolic succession Four Marks of the Church Orthodoxy Organization Autocephaly Patriarchate ...
Read more

Zagreb

Image
This article is about the Croatian capital city. For other uses, see Zagreb (disambiguation). City in City of Zagreb, Croatia Zagreb City Grad Zagreb City of Zagreb Clockwise, from top: St. Mark's Square, Croatian State Archives, Zagreb Tram, Art Pavilion, Cibona & HOTO towers and Croatian National Theatre. Flag Coat of arms Zagreb Location of Zagreb in Croatia Show map of Croatia Zagreb Zagreb (Europe) Show map of Europe Coordinates: 45°49′N 15°59′E  /  45.817°N 15.983°E  / 45.817; 15.983 Coordinates: 45°49′N 15°59′E  /  45.817°N 15.983°E  / 45.817; 15.983 Country   Croatia County City of Zagreb RC diocese 1094 Free royal city 1242 Unified 1850 Subdivisions 17 city districts 218 local committees (70 settlements) Government  • Type Mayor-Council  • Mayor Milan Bandić (BM 365)  • City Assembly 51 members BM 365, ZL, NS-R (14) SDP, GLAS, HNS, HSS, NH-PS (13) ...
Read more

Understanding the information contained in the Deep Space Network XML data?

Image
up vote 1 down vote favorite NASA's Deep Space Network activity can be viewed conveniently at https://eyes.nasa.gov/dsn/dsn.html but if you would like data in a more raw XML form, it can be accessed as described in this answer Below is a small Python script that reads the XML into a list of dictionaries, and saves it to disk as a JSON. The dictionaries are organized at the higher level by dish, then by spacecraft per dish. Question: What are the most-likely meanings of all the data field contained in the Deep Space Network XML data? This is the example url from the other answer, used in the script below: https://eyes.nasa.gov/dsn/data/1365107113.xml def dictify(r,root=True): # https://stackoverflow.com/questions/2148119/how-to-convert-an-xml-string-to-a-dictionary-in-python/30923963#30923963 if root: ret...
Read more