I'm wondering about the difference between small (13mm outer dia) ferrite and the yellow white iron powder toroids. Will the ferrite toroids saturate at 5A current? I'm planning on using the cores for buck converters (mostly 3A at probably below 200KHz). (Sorry for naive questions, I don't know much about inductors.)

These are the ones I am looking at:

Ferrite: https://www.ebay.com/itm/Metal-Core-Power-Inductor-Ferrite-Rings-Toroid-Cord-25x10x15mm/310980203521 (also available in 13mm outer dia)

Iron powder: https://www.ebay.com/itm/7mm-Inner-Diameter-Ferrite-Ring-Iron-Toroid-Cores-Yellow-White-50PCS-LW/181834403242

Most of the buck converters seem to use the yellow white iron powder toroids like this https://www.ebay.com/itm/5Pcs-Toroid-Core-Inductors-Wire-Wind-Wound-mah-100uH-6A-Coil-DIY/221981982278 .

From searching on the internet, the yellow white toroids seem to have a permeability of 75, and the ferrite has a permeability of 2300 or so. Is this important for saturation. I have some toroids and an LCR meter, and the ferrite toroid needs only a few turns of wire to get a 1mH inductor, vs many more turns for the iron powder core. Will this matter if peak current through the inductor is limited?

I'm guessing the ferrite toroids are great at low currents (0-100mA) and low frequencies (<100KHz, as I can get more inductance with fewer turns). But, are they also good for higher currents (like 5-6A peak)?

Any help will be appreciated.

[PS: also another reason I ask, is that at my place, the ferrite cores are half the price of the iron powder cores.]

There is a color standard for painted toroids, and yellow means it has hysteresis to prevent saturation and is meant for filter inductors. But a side effect is that it has very low permeability. Black ferrite is usually a good choice for transformers. Blue is an expensive Permalloy that is more efficient than ferrite. Green is low frequency filters made with silicon steel tape wrapped to form a toroid.

This chart is generic as it is not including fine details such as permeability, and does not state if iron, steel, ferrite or permalloy, which is a nickel-iron alloy.

PC power supplies can put out over 1,000 watts and they use E cores as they are easy to wind by machine, and can have a cross section large enough to handle as much as 10 ampere/turns, and a tiny 10 mil air gap helps a lot. Large toroids need expensive winding machine heads so toroids are better used at low voltages were the number of windings is low, such as car stereo power supplies.

NOTE: Sometimes practical reasons determine what material and shape of transformer are used, which is not always the best choice. Cost and size compete with efficiency. The opinions of engineering and marketing and sales are not the same, and who wins determines what is used. "Just good enough" wins most of the time.

Powdered Iron is Cheap and more forgiving when it comes to saturation due to the more gradual BH curves . There is a down side when for Buck and most other DC/DC convertors . The inductor ripple current will cause more core losses in the powdered iron than in most ferrites . It is quite normal to have AC ripple currents at about 33% of the max DC load current . So on an orthodox hard-switched peak current mode switching regime which most easy to buy chips are specified to do you will get lower efficiency on powdered iron . When I run powdered iron I set up for very low ripple currents to make core losses very low.